Retsch Abrasion Tester AT 100 XL (Bond Index) NEW PRODUCT
Dissolution >> Retsch Abrasion Tester AT 100 XL (Bond Index) NEW PRODUCT
Retsch Abrasion Tester AT 100 XL (Bond Index) NEW
"The Bond Abrasion Index, devised by F.C. Bond in the 1940‘s, quantifies the abrasivity of ores and minerals. The index serves to calculate metal wear rates in crushers and ball consumption rates in ball mills.
The AT 100 XL consists of a rotating insert into which dry ore samples with a defined particle size are placed. An impact paddle mounted on a centre shaft, rotating at a higher speed than the insert, grinds the sample over a defined period of time.
Both insert and paddle rotate in the same direction. The paddle is made from standard alloy steel hardened to 500 Brinell. The Abrasion Index is calculated from the weight loss of the paddle under standard operating conditions." (RETSCH)
Product Advantages:
pre-set rotation speed and time
CE conform version
Features
| Applications | quantification of the abrasivity of ores and minerals |
| Field of application | construction materials, environment / recycling, geology / metallurgy |
| Evaluation | calculation of loss of mass by weighing the paddle |
| Material feed size* | < 19 mm |
| Batch size / feed quantity* | 400 g each process |
| Number of processes | 4, each 400 g |
| Time for abrasivity test | 4*15 min |
| Rotating paddle | 3" x 1" x ¼" hardened to 500 Brinell |
| Rotating speed | impact paddle 632 min-1 / insert 70 min-1 |
| Electrical supply data | 230 V, 50 Hz |
| Power connection | 1-phase |
| W x H x D | 700 x 1140 x 700 mm |
| Net weight | ~ 246 kg |
| Standards | CE |
Please note:
*depending on feed material and instrument configuration/settings
"The Bond Index Abrasion Tester AT 100 XL consists of a rotating insert into which a dry sample with a defined particle size is placed. An impact paddle mounted on a centre shaft rotating at a higher speed than the insert grinds the sample over a defined period of time.
Both insert and paddle rotate in the same direction. The paddle is made from standard alloy steel hardened to 500 Brinell. The Abrasion Index is calculated from the weight loss of the paddle under standard operating conditions." (RETSCH)
For additional details regarding this equipment, please visit http://www.retsch.com/products/assisting/testing/at-100-xl/ to download the product brochure and data sheet.